Preparation of nanoparticle recording media for next-generation magnetic recording

下一代磁记录用纳米颗粒记录介质的制备

• 批准号: 21560348
• 负责人: ISHII Kiyoshi
• 金额: $ 3万
• 依托单位: Utsunomiya University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560348/
• 关键词: 磁気記録媒体; 垂直磁気記録媒体; スパッタ膜; ガスフロースパッタ法; FePt; 垂直磁気記録

In this study, we aimed at the development of nanoparticle magnetic recording media for next-generation recording media. For the purpose, a new sputtering method was used to prepare a FePt alloy thin film having the structures of L10 crystal phase and nanoparticle-assembly. As a result, we found that the FePt thin films with aimed structures and magnetic properties have been grown at the substrate temperature of about 300 ℃. They are considered as a thin film having very high potential as a nanoparticle magnetic recording medium.

在这项研究中，我们旨在开发用于下一代记录介质的纳米颗粒磁记录介质，为此，采用一种新的溅射方法制备具有L10晶相和纳米颗粒组装体结构的FePt合金薄膜。结果，我们发现具有目标结构和磁性能的FePt薄膜在约300℃的衬底温度下生长，它们被认为是具有非常高潜力的纳米颗粒磁记录介质的薄膜。

项目成果

ガスフロースパッタ法によるL10規則化したFePt薄膜における粒子の微細化

气流溅射法细化 L10 有序 FePt 薄膜的颗粒

• 发表时间: 2010
• 作者: 設楽修平; 他
• 通讯作者: 他

STMによる磁性ナノ粒子の磁化反転検出の試み

尝试使用 STM 检测磁性纳米粒子的磁化反转

• 发表时间: 2009
• 作者: 佐久間洋志; 青戸敦; 石井清
• 通讯作者: 石井清

FMR study of Fe nanoparticle chains

Fe 纳米粒子链的 FMR 研究

• 发表时间: 2010
• 作者: H. Sakuma; Y. Sato;K. Ishii
• 通讯作者: K. Ishii

Formation of closely packed grains with L10 ordering in gas-flow-sputtered FePt thin films

在气流溅射 FePt 薄膜中形成具有 L10 排序的紧密堆积晶粒

• 发表时间: 2011
• 作者: Hiroshi Sakuma; 他
• 通讯作者: 他

結晶配向したFePt薄膜の規則度に関する研究

晶体取向FePt薄膜的规律性研究

• 发表时间: 2012
• 作者: 佐藤芳樹;佐久間洋志;石井清
• 通讯作者: 石井清