Material design of cement for increased waste usage and reduction of CO_2 emissions

用于增加废物利用率和减少 CO_2 排放的水泥材料设计

• 批准号: 21560480
• 负责人: SAKAI Etsuo
• 金额: $ 2.75万
• 依托单位: Tokyo Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560480/
• 关键词: 土木材料; 二酸化炭素; 廃棄物資源化; セラミックス; 廃棄物処理; 二酸化炭素削減; 廃棄物再資源化

Cement industry contributes to the recycling of resources by using various industrial wastes and by-products in Japan. This study investigated the influence of the interstitial phase composition and the addition of mineral admixtures on the fluidity and adiabatic temperature rise properties of the cement which contained a greater interstitial phase than ordinary Portland cement. By using cements containing high interstitial phase and mineral admixtures such as blast furnace slag and limestone powder, it is possible to enlarge waste usage and reduce CO_2 emission without changing the performance of cement in cement industry.

日本的水泥工业通过利用各种工业废物和副产品，为资源的循环利用做出了贡献。本研究研究了间隙相组成和矿物掺合料的添加对水泥流动性和绝热温升性能的影响，该水泥含有比普通硅酸盐水泥更多的间隙相。水泥工业中采用高间隙相水泥和高炉矿渣、石灰石粉等矿物掺合料，可以在不改变水泥性能的情况下，扩大废物利用，减少CO_2排放。

项目成果

Material design of cement for increased waste usage and reduction of CO_2 emissions

用于增加废物利用率和减少 CO_2 排放的水泥材料设计

• 发表时间: 2011
• 作者: Etsuo Sakai

廃棄物使用量を増大させたセメントの材料設計と新型熱量計による品質管理手法

使用新型热量计增加废物利用率和质量控制方法的水泥材料设计

• 发表时间: 2010
• 作者: 坂井悦郎;丸屋英二;萩原清市;大門正機
• 通讯作者: 大門正機

被粉砕性の異なる石灰石微粉末を混和したC3A相高含有セメントの流動性

高C3A相水泥掺入不同破碎性石灰石细粉的流动度

• 发表时间: 2011
• 作者: 荻野正貴; 新大軌; 丸屋英二; 浅賀喜与志; 坂井悦郎
• 通讯作者: 坂井悦郎

Fluidity of Blast-Furnace Cement Having Different Aluminate Phase Contents

不同铝酸盐相含量高炉水泥的流动性

• 发表时间: 2009
• 作者: Daiki Atarashi; Etsuo Sakai; Eiji Maruya; Masaki Daimon
• 通讯作者: Masaki Daimon

社会環境マテリアル

社会和环境材料

• 发表时间: 2009
• 作者: 大門正機;坂井悦郎編
• 通讯作者: 坂井悦郎編