High-functionalization of Mechanical Property in Carbon Steels by Giant Straining

通过大应变实现碳钢机械性能的高功能化

• 批准号: 20760467
• 负责人: TODAKA Yoshikazu
• 金额: $ 2.83万
• 依托单位: Toyohashi University of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20760467/
• 关键词: 巨大ひずみ形状不変加工; 結晶粒微細化; 力学特性; 引張特性; 疲労特性; 水素脆化; 格子欠陥; 鉄鋼材料; High-Pressure Torsion; サブミクロン結晶粒組織

In the submicrocrystalline ultra-low carbon steel without special alloy-elements produced by HPT (High-Pressure Torsion) straining which is one of the severe plastic deformation processes, mechanical properties were investigated. In the tensile property, the engineering tensile strength was 1.9 GPa, which is similar to the value of maraging high-alloy steels. The elongation increased with strain, is caused by the reduction of the stress concentration due to the existence of continuously recrystallized grains. Hydrogen embrittlement (HE) occurred in the specimen with the high tensile strength of 1.9 GPa. However, its HE was suppressed via recovery process by annealing at low temperature while maintaining the high strength.

在通过HPT（高压扭转）应变（一种剧烈的塑性变形过程）生产的不含特殊合金元素的亚微晶超低碳钢中，研究了力学性能。拉伸性能方面，工程拉伸强度为1.9GPa，与马氏体时效高合金钢的值相近。伸长率随应变而增加，是由于连续再结晶晶粒的存在而导致应力集中减少而引起的。抗拉强度高达 1.9 GPa 的试样发生氢脆（HE）。然而，在保持高强度的同时，通过低温退火的恢复过程，其HE受到抑制。

项目成果

The dynamic phase transformation and formation of nanocrystalline structure in SUS304 austenitic stainless steel subjected to high pressure torsion

SUS304奥氏体不锈钢在高压扭转下的动态相变和纳米晶结构的形成

• 发表时间: 2008
• 作者: J. G. Li; M. Umemoto; Y.Tod aka; K. Fujisaku;K. Is uchiya
• 通讯作者: K. Is uchiya

Mechanical pro perties of submicrocrystalline IF ste el produced by HPT-straining

HPT 应变生产的亚微晶 IF 钢的力学性能

• 发表时间: 2009
• 作者: Y. Todaka; H. Nagai; Y. Takubo; M. Yoshii; M. Kumagai; M. Umemoto
• 通讯作者: M. Umemoto

Effect of strain gradient and pressure in HPT on the hardening and grain refinement of metals

HPT 中的应变梯度和压力对金属硬化和晶粒细化的影响

• 发表时间: 2009
• 作者: M.Umemoto; Y.Todaka; N.Wu; Y.Ohnishi; H.Azuma; K.Tsuchiya
• 通讯作者: K.Tsuchiya

旋削加工および摩擦加工により形成した超微細結晶粒組織

通过车削和摩擦加工形成的超细晶粒结构

• 发表时间: 2008
• 作者: 永井宏典; 戸高義一; 梅本実
• 通讯作者: 梅本実

高圧下巨大ひずみ加工による圧力誘起相変態を利用した材質制御

通过高压下的大应变处理进行压力诱导相变来控制材料质量

• 发表时间: 2009
• 作者: 戸高義一; 梅本実; 大西由城; 東宏昭; 入江建州; 足立望; 上路林太郎
• 通讯作者: 上路林太郎