Chiral molecular thin films prepared by vapor deposition polymerization with selective adsorption

选择性吸附气相沉积聚合制备手性分子薄膜

• 批准号: 23651090
• 负责人: KUBONO Atsushi
• 金额: $ 2.58万
• 依托单位: Shizuoka University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23651090/
• 关键词: 表面 界面ナノ構造; 薄膜; キラル; 蒸着; ポリアミド; 高分子; 蒸着重合; 選択吸着; 配向; 成膜機構

Thin polymeric films with chirality were prepared by vapor deposition polymerization. Helix structures were formed in the polyamide films from racemic monomers. This resultindicates that the selective adsorption and reaction of a specific optical isomer occurred locally on the substrate and within the bulk. Moreover the quartz crystal microbalance technique realized the in-situ observation of the initial stage in film formation and provides important parameters for molecular adsorption and orientation.

通过气相沉积聚合制备了具有手性的聚合物薄膜。螺旋结构是由外消旋单体在聚酰胺薄膜中形成的。该结果表明特定旋光异构体的选择性吸附和反应发生在基底上和本体内部。此外，石英晶体微天平技术实现了成膜初始阶段的原位观察，为分子吸附和取向提供了重要参数。

项目成果

蒸着重合ポリアミドの水素結合性とモノマー構造の対称性

气相沉积聚合聚酰胺的氢键性能和单体结构对称性

• 发表时间: 2011
• 作者: 上田和茂;尾関遊之;山本希;伊東卓哉;久保野敦史
• 通讯作者: 久保野敦史

有機・高分子薄膜の高次構造制御

有机/聚合物薄膜的高阶结构控制

• 发表时间: 2012
• 期刊: 電子情報通信学会技術報告
• 作者: 久保野敦史

Dipole Orientation in Polymeric Thin Films Prepared by Vapor Deposition Polymerization

气相沉积聚合制备的聚合物薄膜中的偶极子取向

• 发表时间: 2011
• 作者: Toru Yajima;Yingying Yu;Masayuki Futamata;Takuro Tomita;M. Futamata;錦野将元;M. Futamata;M. Futamata;池部雅俊;T. Ito and A. Kubono
• 通讯作者: T. Ito and A. Kubono

有機蒸着薄膜形成過程に及ぼす入射分子温度の影響

入射分子温度对有机气相沉积薄膜形成过程的影响

• 发表时间: 2012
• 作者: Toru Yajima;Yingying Yu;Masayuki Futamata;Takuro Tomita;M. Futamata;錦野将元;M. Futamata;M. Futamata;池部雅俊
• 通讯作者: 池部雅俊