Microstructural control using transformation from metastable structure

利用亚稳态结构的转变进行微观结构控制

• 批准号: 22686070
• 负责人: NAGIRA Tomoya
• 金额: $ 8.57万
• 依托单位: Osaka University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (A)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22686070/
• 关键词: 相変態; 準安定組織; 過冷融液; 過程融液; 準安定共晶; セラミックス

The paper a ims to produce the new ceramics fabrication process through the transformation from the metastable to the equilibrium eutectic structure. The mechanism for the metastable/ equilibrium transformation was discussed based on a thermodynamic approach including the strain energy. In the eutectic system which has Al_2O_3 and perovskite and garnet phases, the effect of kinds of perovskite on the transformation was also examined The Ce doped eutectic casting was demonstrated to be used as a phosphor.

纸本IMS通过从亚稳态到平衡的共晶结构的转化来生成新的陶瓷制造过程。基于包括应变能的热力学方法讨论了亚稳态/平衡转化的机制。在具有AL_2O_3和钙钛矿和石榴石相的共晶系统中，还研究了钙钛矿对转化的类型的影响。

项目成果

一方向Al_2O_3-YAG共晶系に形成される粗大共晶組織の形成

单向Al_2O_3-YAG共晶体系粗大共晶组织的形成

• 发表时间: 2011
• 作者: 原広憲;柳楽知也;秦野了輔;安田秀幸;吉矢真人
• 通讯作者: 吉矢真人

3 D chain structure of unidirectionally solidified eutectic Al_2O_3-YAG-ZrO_2 ceramic composite

单向凝固共晶Al_2O_3-YAG-ZrO_2陶瓷复合材料3D链状结构

• 发表时间: 2010
• 作者: Tomoya Nagira;Hideyuki Yasuda;Satoshi Takeshima;Takumi Sakimura;Yoshiharu Waku;Kentaro Uesugi
• 通讯作者: Kentaro Uesugi

一方向凝固Al_2O_3-YAG共晶系に形成される粗大共晶組織の形成

单向凝固Al_2O_3-YAG共晶体系中粗大共晶组织的形成

• 发表时间: 2011
• 作者: 原広憲;柳楽知也;秦野了輔;安田秀幸;吉矢真人
• 通讯作者: 吉矢真人