A study on evaluation for residual axial force of corroded high strength bolts

腐蚀高强螺栓残余轴向力评估研究

• 批准号: 22560483
• 负责人: SHIMOZATO Tetsuhiro
• 金额: $ 2.83万
• 依托单位: University of the Ryukyus
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22560483/
• 关键词: 腐食; 高力ボルト; 残存軸力; 鋼橋; 維持管理; 摩擦接合継手; 軸力計測; 腐食形状計測; 引張耐力; 疲労耐久性; すべり耐力

The residual axial force of corroded high strength bolts has been investigated. The corroded high strength bolts cut out from a collapsed steel girder bridge were classified from the viewpoints of shape and thickness reduction of nut. The results showed that the residual axial force seems to be affected by the shape, in addition to the thickness reduction. It was analytically indicated that the decrease in an axial force by the thickness reduction is caused by the local deformation of nut edge and hole ci rcumference of splice plate. Moreover, it was revealed that the measurement of the thickness reduct ion near the washer can evaluate the residual axial force.

已经研究了腐蚀的高强度螺栓的残留轴向力。从塌陷的钢梁桥切出的腐蚀的高强度螺栓是从螺母的形状和厚度减小的角度分类的。结果表明，除了减小厚度外，残留的轴向力似乎还受到形状的影响。在分析上表明，厚度减小的轴向力减小是由螺母边缘和孔孔的局部变形引起的剪接板的局部变形。此外，揭示了垫圈附近的厚度还原离子的测量可以评估残留的轴向力。

项目成果

腐食高力ボルトの残存軸力評価に関する実験的研究

腐蚀高强螺栓残余轴向应力评估试验研究

• 作者: 吉田秀典;他;大城進太郎，下里哲弘，有住康則，田井政行
• 通讯作者: 大城進太郎，下里哲弘，有住康則，田井政行

腐食劣化した高力ボルトの残存軸力評価に関する研究

腐蚀高强螺栓残余轴向力评估研究

• 发表时间: 2013
• 期刊: 日本学術会議・土木学会構造工学論文集
• 作者: 下里哲弘;田井政行; 有住康則;矢吹哲哉;長嶺由智
• 通讯作者: 長嶺由智

腐食劣化した高力ボルトの残存軸力推定に関する解析的研究

腐蚀高强螺栓残余轴向力估算的解析研究

• 发表时间: 2012
• 作者: 田井政行; 下里哲弘; 有住康則; 大城進太郎
• 通讯作者: 大城進太郎