Study on corrosion mechanism and residual strength of high strength bolted connection

高强度螺栓连接腐蚀机理及残余强度研究

• 批准号: 21760357
• 负责人: HASHIMOTO Kunitaro
• 金额: $ 3万
• 依托单位: Kyoto University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21760357/
• 关键词: 高力ボルト摩擦接合; 腐食; すべり係数; 残存耐力; ボルト軸力

In this research, to clarify corrosion mechanism of high strength bolted joints and residual strength of the joints damaged by corrosion, corrosion accelerating experiment and slip experiment were carried out. From the tests, it is found that though inner surfaces of the connection are almost corroded, shafts of bolts and near holes of the inner surface are few corroded, and slip strength of the joints are increased due to generation of rust over the inner surfaces, but tensile and yielding strength of the joints are decreased because plate thickness and width are decreased.

在这项研究中，为了澄清高强度螺栓接头的腐蚀机制以及腐蚀损坏的接头的残留强度，进行了加速实验和滑动实验。从测试中可以发现，尽管连接的内表面几乎是腐蚀的，但螺栓的轴和内表面的近孔几乎没有腐蚀，并且关节的滑动强度由于在内表面上产生生锈而提高，但是由于板的厚度和宽度降低了板的拉伸和屈服强度。

项目成果

高カボルト摩擦接合継手の腐食劣化後の残存耐力に関する研究

大功率摩擦焊接头腐蚀劣化后残余强度研究

• 发表时间: 2010
• 作者: 築地貴裕;橋本国太郎;杉浦邦征
• 通讯作者: 杉浦邦征

高力ボルト摩擦接合継手接合面内の腐食挙動に関する実験的研究

高强螺栓摩擦焊接头接合面内腐蚀行为试验研究

• 发表时间: 2010
• 期刊: 鋼構造年次論文報告集(日本鋼構造協会) 第18巻
• 作者: 築地貴裕;橋本国太郎;杉浦邦征
• 通讯作者: 杉浦邦征

高力ボルト摩擦接合継手の腐食劣化後の残存耐力に関する研究

高强螺栓摩擦焊接头腐蚀劣化后残余强度研究

• 发表时间: 2010
• 作者: 築地貴裕;橋本国太郎;杉浦邦征
• 通讯作者: 杉浦邦征

高カボルト摩擦接合面内の腐食性状に関する実験的研究

高伏摩擦接头表面腐蚀特性实验研究

• 发表时间: 2010
• 期刊: 鋼構造年次論文報告集
• 作者: 築地貴裕;橋本国太郎;杉浦邦征
• 通讯作者: 杉浦邦征