Development of high-fracture-toughness and high-hardness Tic Sic ceramics with Ti3SiC2 binder phase

Ti3SiC2粘结相高断裂韧性、高硬度Tic Sic陶瓷的研制

• 批准号: 21560738
• 负责人: TAIMATSU Hitoshi
• 金额: $ 3万
• 依托单位: Akita University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560738/
• 关键词: 粉末冶金; 炭化チタン; 炭化ケイ素; 炭化チタンケイ素; 加圧焼結; ヤング率; 硬さ; 破壊靭性値; 破壊靱性値

To develop high-hardness and high-fracture-toughness ceramics, Ti C-based ceramics were synthesized and consolidated by reaction hot-pressing of BN-Ti-TiC-SiC or TiC-SiC-TiSi_2 powder mixtures. For BN-Ti-TiC-SiC powder mixtures, Ti(C, N)-TiB_2-Ti_5Si_3C_x were synthesized. These ceramics had hardness values below 20 GP_a. For 0.5TiC-0.5SiC-(0.05-0.15)TiSi_2 powder mixtures, dense TiC-SiC-Ti_3SiC_2 ceramics were produced. These ceramics showed good sinterability and were excellent in mechanical properties: hardness 21-22 GPa and fracture toughness 6 MPa _m^<1/2>.

为了开发高硬度和高裂纹 - 阻止陶瓷，通过反应热压BN-TI-TIC-SIC或TIC-SIC-TISI_2粉末混合物合成了基于Ti C的陶瓷。对于Bn-Ti-TiC-SIC粉末混合物，合成了Ti（C，N）-TIB_2-TI_5SI_3C_X。这些陶瓷的硬度值低于20 gp_a。对于0.5TIT-0.5SIC-（0.05-0.15）TISI_2粉末混合物，生产了密集的TIC-SIC-TI_3SIC_2陶瓷。这些陶瓷表现出良好的骨骼性，并且在机械性能方面非常出色：硬度21-22 GPA和断裂韧性6 MPa _M^<1/2>。

项目成果

TiC-SiC-Ti_3SiC_2系セラミックスの合成と機械的性質

TiC-SiC-Ti_3SiC_2陶瓷的合成及力学性能

• 发表时间: 2011
• 作者: 泰松斉;仁野章弘;菅原和久;橋本林娜;杉山重彰
• 通讯作者: 杉山重彰

パルス通電場プロセシング総説集(第7章第2節硬質材料II)

脉冲电流现场加工回顾集（第7章第2节硬质材料II）

• 发表时间: 2010
• 作者: 杉山重彰;泰松斉
• 通讯作者: 泰松斉

チタン系およびタングステン系硬質セラミック材料の開発研究

钛基、钨基硬质陶瓷材料的研发

• 发表时间: 2011
• 期刊: 大阪冶金会会誌
• 作者: Y. Tanaka;J.-M. Yang;S. Kishimoto;Y-F Liu and Y. Kagawa;泰松斉
• 通讯作者: 泰松斉

通電加圧焼結によるTiC-SiCセラミックスの合成とその機械的性質

电流压力烧结制备TiC-SiC陶瓷及其力学性能

• 发表时间: 2010
• 作者: 白賢君;橋本林梛;杉山重彰;仁野章弘;菅原稲久;泰松斉
• 通讯作者: 泰松斉

通電加圧焼結によるTiB_2-Ti(C,N)系複合体の合成とその機械的性質

通电加压烧结TiB_2-Ti(C,N)基复合材料的合成及其力学性能

• 发表时间: 2009
• 作者: 泰松斉;中下弥緒;菅原和久;杉山重彰
• 通讯作者: 杉山重彰