Application of glass-ceramics containing TiO_2 nanocrystals for transparent photocatalytic material

含TiO_2纳米晶微晶玻璃在透明光催化材料中的应用

• 批准号: 19569001
• 负责人: MASAI Hirokazu
• 金额: $ 2.4万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2007
• 资助国家: 日本
• 起止时间: 2007 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-19569001/
• 关键词: ガラス; 結晶化ガラス; 酸化チタン; 光触媒

Transparent glass-ceramics with TiO_2 nanocrystallites have been fabricated. By controlling precipitated size of TiO_2 that possesses high refractive index, high transparency of the glass-ceramics was obtained. Preparation of metastable anatase was observed in transparent TiO_2 glass-ceramics, which indicates that there is a correlation between the chemical composition of glass and the precipitated crystalline phase. On the other hand, we examined surface structural change by pulsed laser irradiation or chemical treatment. These results have shown that the present TiO_2 glass-ceramic can be a candidate for transparent photocatalytic material.

已制造了带有TIO_2纳米晶体的透明玻璃陶瓷。通过控制具有高折射率的TIO_2的沉淀大小，获得了玻璃陶瓷的高透明度。在透明的TIO_2玻璃陶瓷中观察到亚稳态的制备，这表明玻璃的化学成分与沉淀的结晶相之间存在相关性。另一方面，我们通过脉冲激光照射或化学处理检查了表面结构变化。这些结果表明，目前的TIO_2玻璃陶瓷可以成为透明光催化材料的候选者。

项目成果

結晶化ガラス、それを用いた光触媒部材及びそれを用いた光学部材

结晶玻璃、使用其的光催化部件以及使用其的光学部件

• 发表时间: 2009

酸化チタン結晶化ガラスの作製と結晶化挙動

二氧化钛微晶玻璃的制备及晶化行为

• 发表时间: 2008
• 作者: 正井博和;高橋儀宏;藤原巧;小松高行
• 通讯作者: 小松高行

チタニアナノ結晶化ガラスにおける結晶相と組成の検討

二氧化钛纳米晶玻璃的晶相和成分研究

• 发表时间: 2007
• 作者: 金森英児;正井博和;高橋儀宏;藤原巧
• 通讯作者: 藤原巧

光ファイバ型デバイス用高機能性結晶化ガラスの開発

光纤器件用高性能微晶玻璃的开发

• 发表时间: 2008
• 作者: 正井博和;高橋儀宏;藤原巧;Hirokazu Masai;正井博和;正井博和
• 通讯作者: 正井博和

酸化チタン透明ナノ結晶化ガラスの創製 一時空間レーザー結晶化法によるガラスベース未来材料

利用时空激光晶化方法制造二氧化钛透明纳米晶玻璃玻璃基未来材料

• 发表时间: 2008
• 期刊: 未来材料 8
• 作者: H. Masai;S. Mizuno;T. Fujiwara;H. Mori;T. Komatsu;Hirokazu Masai;Hirokazu Masai;Hirokazu Masai;藤原巧
• 通讯作者: 藤原巧