New electrochemical approach for evaluation of corrosion behavior of dental alloy

评估牙科合金腐蚀行为的新电化学方法

• 批准号: 19390500
• 负责人: ODA Yutaka
• 金额: $ 9.32万
• 依托单位: Tokyo Dental College
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2007
• 资助国家: 日本
• 起止时间: 2007 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-19390500/
• 关键词: 歯科用合金; 腐食; 電気化学; チタン; タンパク質; 貴金属合金; 変色

Although well known for their superior resistance to corrosion, titanium and titanium alloys are unable to withstand discoloration in clinically. This study revealed the corrosion behavior of titanium alloys with electrochemical measurement, discoloration, dissolution, EQCM and EIS analysis. The results confirm that corrosion of titanium takes place in acidulated fluoride- or alkaline peroxide-containing solution, and discoloration mainly results from peroxide-induced oxidation in acidulated peroxide containing solution. The addition of chromium suppresses corrosion of titanium alloys.

尽管钛和钛合金以其优异的耐腐蚀性而闻名，但在临床上却无法承受变色。本研究通过电化学测量、变色、溶解、EQCM 和 EIS 分析揭示了钛合金的腐蚀行为。结果证实，钛的腐蚀发生在酸化的含氟化物或碱性过氧化物的溶液中，变色主要是由于酸化的含过氧化物的溶液中过氧化物诱导的氧化所致。添加铬可抑制钛合金的腐蚀。

项目成果

アルカリ性過酸化水素含有溶液中でのチタン合金の電気化学的腐食挙動

钛合金在碱性过氧化氢溶液中的电化学腐蚀行为

• 发表时间: 2008
• 作者: 武本真治;服部雅之;吉成正雄;河田英司;小田豊
• 通讯作者: 小田豊

過酸化水素を含むアルカリ性溶液中でのチタン合金の変色

钛合金在含有过氧化氢的碱性溶液中变色

• 发表时间: 2009
• 作者: 武本真治;服部雅之;吉成正雄;河田英司;小田豊
• 通讯作者: 小田豊

アルカリ性過酸化水素含有溶液中での純チタンの耐食性

纯钛在含碱性过氧化氢溶液中的耐腐蚀性能

• 发表时间: 2008
• 作者: 武本真治;服部雅之;松本倫彦;吉成正雄;河田英司;小田豊
• 通讯作者: 小田豊

Surface oxide film formation on titanium alloys immersed in acidic saline solutions containing hydrogen peroxide

含过氧化氢的酸性盐溶液中钛合金表面氧化膜的形成

• 发表时间: 2009
• 期刊: Bioceramics 22 22
• 作者: S.Takemoto;M.Hattori;M.Yoshinari;E.Kawada;Y.Oda
• 通讯作者: Y.Oda

Surface reaction of Ti-Cr alloys in a fluoride-containing solution, Proceedings of the 6th International Symposium on titanium in Dentistry, 99

Ti-Cr合金在含氟溶液中的表面反应，第六届国际牙科钛研讨会论文集，99

• 发表时间: 2007
• 作者: Takemoto S;Hattori M;Yoshinari M;Kawada E;Oda Y
• 通讯作者: Oda Y