Development and deployment of silica thin film coating method in the mouth with biosafety

具有生物安全性的口腔二氧化硅薄膜涂层方法的开发和部署

• 批准号: 24792046
• 负责人: TANAKA Takahiro
• 金额: $ 2.66万
• 依托单位: Kanagawa Dental College
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2012
• 资助国家: 日本
• 起止时间: 2012-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-24792046/
• 关键词: シリカガラスコーティング; 齲蝕予防; セラミックス; レーザー; 耐酸性; 耐摩耗性; シリカコーティング

If the tooth surface is covered with a colorless transparent silica thin film, it can be expected to prevent caries. The purpose of this study was to use the pre-ceramic polymer perhydropolysilazane (PHPS) as a silica precursor to form a silica thin film on the tooth surface, and build silica coating method of biological safety. The PHPS to silica thin film coating was analyzed to wear resistance and acid resistance. As a result, the silica thin film was obtained chemical durability and mechanical strength.

如果牙齿表面覆盖一层无色透明的二氧化硅薄膜，就有望预防龋齿。本研究的目的是利用陶瓷前体聚合物全氢聚硅氮烷（PHPS）作为二氧化硅前体，在牙齿表面形成二氧化硅薄膜，构建生物安全的二氧化硅涂层方法。对 PHPS 二氧化硅薄膜涂层的耐磨性和耐酸性进行了分析。结果，二氧化硅薄膜获得了化学耐久性和机械强度。

项目成果

シリカ薄膜コーティング法がセリア系ナノジルコニアとレジンセメントの接着強さに及ぼす影響

二氧化硅薄膜包覆方法对二氧化铈基纳米氧化锆与树脂水门汀粘结强度的影响

• 发表时间: 2012
• 作者: 田中隆博; 山口益司; 竹田仁一; 高島志保; 進藤豊彦; 寺中敏夫
• 通讯作者: 寺中敏夫

Silica thin film coating improves bond strength of Ce-TZP/alumina nanocomposite

二氧化硅薄膜涂层提高了 Ce-TZP/氧化铝纳米复合材料的结合强度

• 发表时间: 2012
• 作者: T. TANAKA; M. YAMAGUCHI; T. SHINDO; T. TERANAKA
• 通讯作者: T. TERANAKA

ペルヒドロポリシラザンを用いた歯面および歯科材料へのシリカコーティング法の開発と評価

使用全氢聚硅氮烷用于牙齿表面和牙科材料的二氧化硅涂层方法的开发和评估

• 发表时间: 2013
• 作者: 田中隆博; 山口益司; 竹田仁一; 高島志保; 進藤豊彦; 寺中敏夫
• 通讯作者: 寺中敏夫

ガラス薄膜による根面齲蝕予防コーティング

玻璃薄膜防牙根龋涂层

• 发表时间: 2012
• 作者: 田中隆博; 山口益司; 竹田仁一; 高島志保; 進藤豊彦; 寺中敏夫
• 通讯作者: 寺中敏夫

歯根象牙質へのシリカコーティング

根部牙本质上的二氧化硅涂层

• 发表时间: 2012
• 作者: 田中隆博; 山口益司; 竹田仁一; 高島志保; 進藤豊彦; 寺中敏夫
• 通讯作者: 寺中敏夫