Nanocrystallized cemented carbide fabricated by friction stir processing

搅拌摩擦加工制备纳米晶硬质合金

• 批准号: 23760707
• 负责人: YOSHIAKI Morisada
• 金额: $ 2.75万
• 依托单位: Osaka University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2013
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23760707/
• 关键词: 摩擦攪拌プロセス; 超硬合金; 摩擦攪拌; 溶射; 組織微細化

The cemented carbide layer was successfully modified by Friction Stir Processing (FSP). The defects in the cemented carbide layer disappeared, and the WC particles were densely packed. It is considered that the plastic flow of the metal binder induced by the FSP led to the rearrangement of the WC particles. The grains of the metal binder were refined to ~200 nm. Additionally, the various metals contained hard particles were also successfully modified by FSP.

通过搅拌摩擦加工（FSP）成功地对硬质合金层进行了改性。硬质合金层中的缺陷消失，WC颗粒堆积致密。据认为，FSP 引起的金属粘结剂的塑性流动导致了 WC 颗粒的重新排列。金属粘合剂的晶粒细化至~200 nm。此外，各种含有硬质颗粒的金属也通过FSP成功改性。

项目成果

Microstructural evaluation of friction stir processed D2 tool steel

搅拌摩擦加工 D2 工具钢的显微组织评价

• 发表时间: 2012
• 作者: T. Nagaoka; H. Watanabe; M. Fukusumi; T. Mizumo; G. Abe; Y. Morisada;H. Fujii
• 通讯作者: H. Fujii

Effect of Tool Geometry on Hardened Layer of Friction Stir Processed Cast Iron

刀具几何形状对搅拌摩擦加工铸铁硬化层的影响

• 发表时间: 2012
• 影响因子: 1.2
• 作者: K. Imagawa; H. Fujii; Y. Morisada; Y. Yamaguchi; S. Kiguchi
• 通讯作者: S. Kiguchi

Surface hardening of ferritic spheroidal graphic cast iron by friction stir processing

铁素体球墨铸铁的搅拌摩擦加工表面硬化

• 发表时间: 2012
• 作者: K. Imagawa; H. Fujii; Y. Morisada; Y. Yamaguchi;S. Kiguchi
• 通讯作者: S. Kiguchi

反応性および非反応性粒子の添加を伴うステンレス鋼への摩擦攪拌プロセス

添加反应性和非反应性颗粒的不锈钢搅拌摩擦工艺

• 发表时间: 2013
• 作者: 木元 慶久; 長岡 亨; 渡邉 博行; 福角 真男; 森貞 好昭; 藤井 英俊
• 通讯作者: 藤井 英俊

摩擦攪拌プロセスを施したステライトの母材結晶粒径に及ぼす晶出炭化物の影響

搅拌摩擦过程中结晶碳化物对司太莱基体晶粒尺寸的影响

• 发表时间: 2012
• 作者: 北村 優介;水野 雅;阿部 源隆;森貞 好昭;藤井 英俊;長岡 亨;福角 真男
• 通讯作者: 福角 真男