Oxidation layer Removal of Metal Surface which Used Electrolyzed Oxidizing Water

使用电解氧化水去除金属表面氧化层

• 批准号: 22560717
• 负责人: SATO Unkai
• 金额: $ 2.91万
• 依托单位: Shinshu University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22560717/
• 关键词: 電解酸化水; 酸化皮膜除去; エッチング性能; ミクロ形状; 純金属; 合金; 電極材料; イリジウム電極; 白金電極; 溶存塩素濃度; 溶存酸素濃度; 金属表面; エッチング作用; 材料加工・処理; 微細加工; 環境対応; 純ニッケル材; 無酸素銅材; 鉄とニッケルの合金; 純鉄材

This paper describes the elucidation about the removal of metal material (pure metal and alloy) of surface oxidation layer using dilute electrolyzed oxidizing water. First, we clarified the etching characteristic of electrolyzed oxidizing water to metal material by immersing experiment. The results showed that electrolyzed oxidizing water has the good etching performance compared with chemical. Next, it processed in the oxidation layer removal by the immersion to electrolyzed oxidizing water and chemical, and surface analysis of samples. The results indicate that electrolyzed oxidizing water can, indeed, be applied to remove metal material surface oxidation layer.

本文对利用稀电解氧化水去除金属材料（纯金属和合金）表面氧化层进行了阐述。首先，通过浸泡实验明确了氧化电解水对金属材料的蚀刻特性。结果表明，与化学腐蚀相比，电解氧化水具有良好的腐蚀性能。接下来，通过电解氧化水的浸渍和化学处理来去除氧化层，并对样品进行表面分析。结果表明，电解氧化水确实可以用于去除金属材料表面氧化层。

项目成果

78パーマロイ材の表面に及ぼすNaCl 電解酸化水の影響

78 NaCl电解氧化水对坡莫合金材料表面的影响

• 发表时间: 2013
• 作者: 佐藤運海;竹ノ内敏一;川久保英樹
• 通讯作者: 川久保英樹

無酸素銅材の表面に及ぼす Na2SO4 電解酸化水の影響

Na2SO4电解氧化水对无氧铜材料表面的影响

• 发表时间: 2012
• 作者: 佐藤運海;竹ノ内敏一;池田由佳;北川大貴;川久保英樹
• 通讯作者: 川久保英樹

高炭素鋼の表面に及ぼす希薄NaCl電解還元水の影響

稀NaCl电解还原水对高碳钢表面的影响

• 发表时间: 2012
• 作者: 佐藤 運海

電解酸化水を用いたFe-42wt%Ni合金の表面酸化皮膜の除去

电解氧化水去除Fe-42wt%Ni合金表面氧化膜

• 发表时间: 2010
• 作者: 佐藤運海; 竹ノ内敏一; 山崎隆夫
• 通讯作者: 山崎隆夫

電解水を用いた洗浄・エッチングおよび防錆

使用电解水进行清洁/蚀刻和防锈

• 发表时间: 2011
• 作者: 佐藤運海