Development and application of carbon nanotube-alumina composites

碳纳米管-氧化铝复合材料的开发及应用

• 批准号: 21560709
• 负责人: OMORI Mamoru
• 金额: $ 2.75万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560709/
• 关键词: カーボンナノチューブ; アルミナ; 複合材料; 放電プラズマ焼結; 水酸化アルミニウム; 人工股関節; 電磁波吸収; 肉厚多層カーボンナノチューブ; 前躯体; 無加圧焼結

We succeeded to prepare a carbon nanotube-alumina composite with good mechanical properties. The composite was characterized by microwave absorption. The composite of 25 mm in length was illuminated in microwave oven after several seconds its irradiation. The composite easily coated with graphite film of which friction coefficient is the lowest in materials. Commercial materials such as microwave absorber, antenna, dust-free alumina, self-lubricating bearing and acetabular cup in total hip joint replacement can be developed from the composite.

我们成功制备了具有良好机械性能的碳纳米管-氧化铝复合材料。通过微波吸收对复合材料进行了表征。长度为25mm的复合材料在照射几秒后在微波炉中照射。该复合材料易于涂覆石墨膜，其摩擦系数是材料中最低的。该复合材料可开发出微波吸收体、天线、无尘氧化铝、自润滑轴承、全髋关节置换术中的髋臼杯等商业材料。

项目成果

Effects of Sintering Additive on Mechanical Properties of Alumina Matrix Composites Reinforced with Carbon Nanotubes

烧结添加剂对碳纳米管增强氧化铝基复合材料力学性能的影响

• 发表时间: 2010
• 作者: G.Yamamoto; M.Omori; T.Hashida; H.Kimura; T.Takag
• 通讯作者: T.Takag

カーボンナノチューブーアルミナ系ナノ複合材料の開発研究

碳纳米管-氧化铝纳米复合材料的研究与开发

• 发表时间: 2009
• 作者: 大森守;山本剛;橋田俊之;大久保昭;木村久道
• 通讯作者: 木村久道

カーボンナノチューブ/アルミナ複合材料の作製と破壊機構の解明に関する研究

碳纳米管/氧化铝复合材料的制备研究及断裂机理的阐明

• 发表时间: 2011
• 作者: 白須圭一; 山本剛; 大森守; 高木敏行; 橋田俊之
• 通讯作者: 橋田俊之

Preparation and Microstructure of Carbon Nanotube-Toughened Alumina Composites

碳纳米管增韧氧化铝复合材料的制备及微观结构

• 发表时间: 2009
• 作者: G. Yamamoto; T. Hashida; M. Omori;H. Kimura
• 通讯作者: H. Kimura

Nanocomposite Prepared from Carbon Nanotubes and Hydroxyapatite Precursors

由碳纳米管和羟基磷灰石前体制备的纳米复合材料

• 发表时间: 2009
• 作者: M. Omori; T. Watanabe; M. Tanaka; A. Okubo; H. Kimura;T. Hashida
• 通讯作者: T. Hashida