High Speed Reaction Field of Stable/ Metastable Phases Mixed in Nano-scale and Its Applications

纳米级稳定/亚稳相混合高速反应场及其应用

• 批准号: 19106014
• 负责人: MATSUO Shinya
• 金额: $ 67.06万
• 依托单位: Osaka University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (S)
• 财政年份: 2007
• 资助国家: 日本
• 起止时间: 2007 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-19106014/
• 关键词: 希土類酸化物; セリア; 蛍石類似構造; 排ガス触媒; メタン水蒸気改質; 脱白金; 混合相状態; 準安定相; 酸素吸蔵能; 水蒸気改質; ナナ空間; メタン改質; ナノ空間

Several resembling CaF_2-like phases could coexist in the Zr-Ce-Pr-O system which were originated from the Zr-Ce-O and Zr-Pr-O systems. When the analogous particles with appropriate compositions are connected coherently by sintering, oxygen deficient-sites may be introduced and on the contrary oxygen intercalation may also occur in the interface region. When optimizing the phenomena, complex oxides involving stable/ metastable phases have demonstrated their potentials as superior reaction fields for exhaust gas catalyst and methane-steam reforming.

Zr-Ce-Pr-O体系中可以共存多种类似CaF_2的相，这些相源自Zr-Ce-O和Zr-Pr-O体系。当具有适当组成的类似颗粒通过烧结连贯地连接时，可能会引入缺氧位点，相反，在界面区域也可能发生氧嵌入。在优化现象时，涉及稳定/亚稳定相的复合氧化物已证明其作为废气催化剂和甲烷蒸汽重整的优异反应领域的潜力。

项目成果

Niを担持した(1-x) ZrO_ CeO_2系酸化物触媒によるメタン水蒸気改質

使用Ni负载(1-x) ZrO_<2-x> CeO_2基氧化物催化剂进行甲烷蒸汽重整

• 发表时间: 2009
• 作者: 松尾伸也;杉村和昭;室田忠俊;小俣孝久
• 通讯作者: 小俣孝久

新しい相状態:カッパドキア相状態の出現とその概念

新相态：卡帕多西亚相态的出现和概念

• 发表时间: 2009
• 作者: 松尾伸也

触媒

催化剂

• 发表时间: 2011

セリア系複合酸化物のナノ空間構造と触媒担体としての特性

二氧化铈基复合氧化物的纳米空间结构及其作为催化剂载体的性能

• 发表时间: 2011
• 作者: 松尾伸也

新規な蛍石型Pr_Zr_O_相の酸素放出挙動

新型萤石型Pr_<0.75>Zr_<0.25>O_<2-y>相的释氧行为

• 发表时间: 2008
• 作者: 松尾伸也