Development of a novel flux method for the synthesis of nitrides with single crystal form.

开发一种用于合成单晶氮化物的新型助熔剂方法。

• 批准号: 23655206
• 负责人: KAWAMURA fumio
• 金额: $ 2.41万
• 依托单位: National Institute for Materials Science
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Challenging Exploratory Research
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011 至 2013
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23655206/
• 关键词: 窒化物; 単結晶; フラックス法; 窒化スカンジウム; 窒化タングステン; 酸窒化物; 新物質; 単相合成; 超高圧; 窒素; HIP; 熱間等方圧加圧

The synthesis of tungsten nitride was tried in Pb flux. As a result, WO3, W-O-N and W-N crystals seems to be synthesized in Pb flux. The XRD profiles of W-N and W-O-N compounds were not attributed to the known pettern. These results might indicate that these substances were new materials.The synthesis of ScN crystals were tried in In-Sc flux system, to which the high-pressure nitrogen gas was dissolved as the nitrogen source. As a result, ScN single crystals with no impurities could be obtained. The yields of ScN was almost 100 % against the Sc source.

在PB通量中尝试了氮化钨的合成。结果，WO3，W-O-N和W-N晶体似乎是在PB通量中合成的。 W-N和W-O-N化合物的XRD轮廓并非归因于已知的Pettern。这些结果可能表明这些物质是新材料。在SC INC通量系统中尝试了SCN晶体的合成，将高压氮气溶解为氮源。结果，可以获得无杂质的SCN单晶。 SCN的产量几乎为100％，而SC源的产量为100％。

项目成果

高圧合成による遷移金属窒化物系新規超硬質材料の探索

高压合成寻找基于过渡金属氮化物的新型超硬材料

• 发表时间: 2013
• 作者: 川村史朗;遊佐斉;谷口尚
• 通讯作者: 谷口尚

高圧下複分解反応における窒化タングステン結晶合成

高压复分解反应合成氮化钨晶体

• 发表时间: 2012
• 作者: 川村史朗;遊佐斉;谷口尚
• 通讯作者: 谷口尚

高圧下複分解反応による新規5d遷移金属窒化物合成

高压复分解反应合成新型5d过渡金属氮化物

• 发表时间: 2011
• 作者: 川村史朗;遊佐斉;谷口尚
• 通讯作者: 谷口尚

六方晶窒化タングステン系焼結体の製造方法及び六方晶窒化タングステン系焼結体

六方晶氮化钨烧结体的制造方法及六方晶氮化钨烧结体

• 发表时间: 2013

高圧下複分解反応による新規 5d 遷移金属窒化物合成

高压复分解反应合成新型5d过渡金属氮化物

• 发表时间: 2011
• 作者: 川村史朗;遊佐斉;谷口尚
• 通讯作者: 谷口尚