Photopolymerization induced phase separation for functional networks polymer thin film

功能网络聚合物薄膜的光聚合诱导相分离

• 批准号: 22760587
• 负责人: KENTARO Taki
• 金额: $ 2.75万
• 依托单位: Kyoto University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22760587/
• 关键词: 多孔構造体; UV硬化; 一方向凍結; 紫外線硬化樹脂; 多孔材料; 凍結; 架橋; 高分子; 相分離; 結晶

In this study, a solution of UV curable monomer and 1, 4-dioxane was frozen unidirectionally and cured by UV irradiation to create a porous monolith structure using the crystals of the frozen solvent as the template materials for the UV curable monomers. The solution viscosity was found to be an important factor to control the pore diameters. As the viscosity affects the diffusivity of the solute, which was UV curable monomer, the combination of the materials and thermal diffusion determines the final porous structure at the interface of crystals.

在这项研究中，紫外可固化的单体和1的溶液在单向上冷冻，并通过紫外线辐照固化，以使用冷冻溶剂的晶体作为紫外可固化的单体的模板材料来创建多孔的单片结构。发现溶液粘度是控制孔径的重要因素。由于粘度会影响溶质的扩散率，即紫外可固化的单体，因此材料的组合和热扩散决定了晶体界面处的最终多孔结构。

项目成果

液-液相分離現象と一方向凍結法を利用した多孔構造体の構造制御

利用液-液相分离现象和单向冷冻方法控制多孔结构

• 发表时间: 2011
• 作者: 岡地理佳;瀧健太郎;長嶺信輔;大嶋正裕
• 通讯作者: 大嶋正裕

Freezing Transient Structure of Phase Separation during Photopolymeri zation-Induced Bubble Nucleation and Growth

光聚合诱导气泡成核和生长过程中相分离的冷冻瞬态结构

• 发表时间: 2010
• 作者: 岡地理佳;瀧健太郎;長嶺信輔;大嶋正裕;小倉鉄平;瀧健太郎;小倉鉄平;小倉鉄平;瀧健太郎
• 通讯作者: 瀧健太郎

紫外線硬化樹脂の硬化速度が発泡体構造に及ぼす影響

UV固化树脂固化速度对泡沫结构的影响

• 发表时间: 2010
• 作者: 岡地理佳;瀧健太郎;長嶺信輔;大嶋正裕;小倉鉄平;瀧健太郎
• 通讯作者: 瀧健太郎

溶媒2成分高分子溶液の一方向凍結過程での相分離挙動と創製される多孔構造

双溶剂聚合物溶液单向冷冻过程中的相分离行为和产生的多孔结构

• 发表时间: 2012
• 作者: 岡地理佳;瀧健太郎;長嶺信輔;大嶋正裕
• 通讯作者: 大嶋正裕

Preparationof Cross-linked Micrometer-scale PorousHoneycomb Monolith from UV Curable Monomer/Dioxane Solution via Unidirectional Freezing and UVIrradiation

紫外光固化单体/二恶烷溶液单向冷冻和紫外辐射制备交联微米级多孔蜂窝整体料

• 发表时间: 2010
• 作者: Okaji;Rika;Kentaro Taki;Shinsuke Nagamine;Masahiro Ohshima
• 通讯作者: Masahiro Ohshima