Examination of new type of grain-refinement process via martensitic microstructure-phase transformation in airplane Ti alloy

飞机钛合金马氏体显微组织相变新型晶粒细化工艺的检验

• 批准号: 22760551
• 负责人: MATSUMOTO Hiroaki
• 金额: $ 2.66万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22760551/
• 关键词: 航空機Ti合金; マルテンサイト; 相分解; 組織制御; チタン合金; マルテンサイト変態; 低温熱処理; 熱間加工; 強度; 室温延性

Microstructural evolution during deformation-heat treatment process of martensite microstructure of airplane Ti alloy was evaluated in this work. Refined microstructure is obtained after cold working in α'-Ti-V-Al alloys and high-strengthening is achieved by combining the fine β precipitation under low temperature-heat treatment. Furthermore, homogeneous martensiticmicrostructure is found to be appeared by high speed deformation at more than 900℃ due to high accumulation of dislocations.

本文对飞机钛合金马氏体显微组织在变形热处理过程中的显微组织演变进行了评价，α'-Ti-V-Al合金经冷加工后获得了细化的显微组织，并通过结合细小的β析出实现了高强度化。此外，在低温热处理下，由于位错的大量积累，在900℃以上的高速变形中出现了均匀的马氏体组织。

项目成果

航空機用Ti-5Al-5Mo-5V-3Cr合金の高温変形挙動と組織変化

航空用Ti-5Al-5Mo-5V-3Cr合金高温变形行为及显微组织变化

• 发表时间: 2012
• 作者: 赤沼俊之;松本洋明;千葉晶彦;稲垣育宏;白井義久;前田尚志
• 通讯作者: 前田尚志

Enhancement of athermal α" martensitic transformation in Ti-10V-2Fe-3Al alloy due to high-speed hot deformation

• DOI: 10.1016/j.scriptamat.2012.03.011
• 发表时间: 2012-07-01
• 期刊: SCRIPTA MATERIALIA
• 影响因子: 6
• 作者: Akanuma, Toshiyuki;Matsumoto, Hiroaki;Maeda, Takashi
• 通讯作者: Maeda, Takashi

Ti-10V-2Fe-3Al合金の熱間加工後の微細組織形成とマルテンサイト変態

Ti-10V-2Fe-3Al合金热加工后显微组织形成及马氏体转变

• 作者: 赤沼俊之;松本洋明;李云平;千葉晶彦;稲垣育宏;白井善久;前田尚志
• 通讯作者: 前田尚志