Fabrication and properties of a hybrid solar-thermoelectric device on Ti-based metal oxides

钛基金属氧化物混合太阳能热电器件的制备和性能

• 批准号: 22760030
• 负责人: TAKAMURA Koji
• 金额: $ 2.58万
• 依托单位: Asahikawa National College of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22760030/
• 关键词: 結晶成長; 太陽電池; 熱電材料; 半導体物性; 酸化物; 色素増感; 色素増感太陽電池; 酸化物半導体; 表面・界面物性; 薄膜・界面物性

A novel hybrid solar-thermoelectric device on Ti-based metal oxides, TiO2 and SrTiO3, has been investigated. SrTiO3 thin films were deposited by RF sputtering in the presence of Ar sputtering gas without oxygen gas. X-ray diffraction pattern indicates that annealed thin films were partially polycrystalline and/or amorphous. A dye-sensitized solar cell, whose electrode is made of thermoelectric material SrTiO3:Nb single crystal, shows photovoltaic and thermoelectric effects.

研究了一种基于钛基金属氧化物 TiO2 和 SrTiO3 的新型混合太阳能热电装置。在没有氧气的 Ar 溅射气体存在下，通过射频溅射沉积了 SrTiO3 薄膜。 X射线衍射图表明退火的薄膜是部分多晶的和/或非晶的。一种染料敏化太阳能电池，其电极由热电材料SrTiO3:Nb单晶制成，表现出光伏和热电效应。

项目成果

酸素無供給下で成長したSrTiO3-Nb薄膜とTiO2/SrTiO3二層膜のポストアニール効果

无氧条件下生长的SrTiO3-Nb薄膜和TiO2/SrTiO3双层膜的后退火效应

• 发表时间: 2012
• 作者: 竹内智彦;久保樹;田村広和;篁耕司;吉本健一
• 通讯作者: 吉本健一

酸素無供給下でのSrTiO_3-Nb薄膜の成長とアニール効果

无供氧条件下SrTiO_3-Nb薄膜的生长及退火效果

• 发表时间: 2011
• 作者: 竹内智彦;菅野隆太郎;後藤竜介;篁耕司;吉本健一
• 通讯作者: 吉本健一

色素増感太陽電池におけるTiO2電極の導電膜の研究

染料敏化太阳能电池TiO2电极导电薄膜的研究

• 发表时间: 2013
• 作者: 駒場俊介;篁耕司
• 通讯作者: 篁耕司

酸素無供給下でのSrTiO3-Nb薄膜の成長とアニール効果

无供氧条件下SrTiO3-Nb薄膜的生长及退火效果

• 发表时间: 2011
• 作者: 竹内智彦;菅野隆太郎;後藤竜介;篁耕司;吉本健一
• 通讯作者: 吉本健一

酸素無供給下でのRFスパッタリング法によるSrTiO3-Nb薄膜の作製と評価

无供氧射频溅射法制备SrTiO3-Nb薄膜并评价

• 发表时间: 2012
• 作者: 竹内智彦;篁耕司;吉本健一
• 通讯作者: 吉本健一