Growth process of martensite in Fe alloys with graded microstructure

梯度组织铁合金中马氏体的长大过程

• 批准号: 21760553
• 负责人: SATO Hisashi
• 金额: $ 2.91万
• 依托单位: Nagoya Institute of Technology
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21760553/
• 关键词: 相変態; 鉄鋼材料; EBSD; 傾斜機能材料; マルテンサイト; 結晶方位関係; 摩擦摩耗; 巨大ひずみ; 組織; 成長

Growth process of butterfly-type martensite is investigated by using Fe-Ni alloy with graded microstructure. The Fe-Ni alloy specimens with graded microstructure are made by the sub-zero treatment under graded temperature or the deformation with graded strain distribution. Characters of martensite depend on not only martensitic transformation temperature but also temperature during its growth. In addition, it is found that the character of martensite is determined by accommodation process for transformation strain under its formation and growth process.

通过将Fe-Ni合金与分级微结构一起研究，研究了蝴蝶型马氏体的生长过程。具有分级微观结构的Fe-Ni合金样品是通过在渐变温度下的零下处理或分级应变分布的变形来制成的。马氏体的特征不仅取决于马氏体变化温度，还取决于其生长期间的温度。此外，发现马氏体的特征取决于其形成和生长过程中转化应变的适应过程。

项目成果

Fe-Ni合金に生成するマルテンサイト相の3次元可視化

Fe-Ni 合金中生成的马氏体相的 3D 可视化

• 发表时间: 2011
• 作者: 田中智幸;佐藤尚;三浦永理;渡辺義見;足立吉隆
• 通讯作者: 足立吉隆

Formation behavior of deformation-induced layer in Fe-Ni alloy by sliding wear and shot peening

Fe-Ni合金滑动磨损与喷丸变形诱发层的形成行为

• 发表时间: 2010
• 作者: H.Sato;T.Nishiura;Y.Kubota;E.M.Fujiwara;Y.Watanabe
• 通讯作者: Y.Watanabe

Fe-30mass%Ni合金の摩耗中における変態挙動と塑性変形挙動

Fe-30mass%Ni合金磨损过程中的相变行为和塑性变形行为

• 发表时间: 2009
• 作者: 窪田優一;佐藤尚;三浦永理;渡辺義見
• 通讯作者: 渡辺義見

Effects of phase transformation temperature on formation of wear-induced layer in Fe-Ni alloys

相变温度对Fe-Ni合金磨损诱发层形成的影响

• 发表时间: 2010
• 作者: H.Sato;Y.Kubota;E.M.Fujiwara;Y.Watanabe
• 通讯作者: Y.Watanabe

Fe-30%Ni合金におけるバタフライマルテンサイト組織のその場変形EBSD観察

Fe-30%Ni合金中蝶形马氏体组织的原位变形EBSD观察

• 发表时间: 2009
• 作者: 佐藤尚;Stefan Zaefferer;渡辺義見
• 通讯作者: 渡辺義見