Improving Fatigue Strength of Welded Joints by Laser Peening

通过激光喷丸提高焊接接头的疲劳强度

• 批准号: 21360214
• 负责人: SAKINO Yoshihiro
• 金额: $ 11.65万
• 依托单位: Osaka University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21360214/
• 关键词: レーザピーニング; 溶接; 疲労; 残留応力; 大型試験体

Nozzle-type laser peening unit, which can apply to welding joints of large steel structures, was developed in this study. Then, it was elucidated by residual stress measurement that large and deep compressive residual stress was also generated by nozzle-type laser peening. Moreover, improving fatigue strength of welded joints after laser peening was ascertained by conducting fatigue tests using large specimens.

在本研究中，开发了喷嘴型激光镀皮单元，可应用于大型钢结构的焊接接头。然后，通过残留应力测量来阐明，喷嘴型激光乳皮也产生了大而深的残留应力。此外，通过使用大型标本进行疲劳测试来确定激光乳头后焊接接头的疲劳强度。

项目成果

大型溶接試験体におけるレーザピーニングの疲労寿命向上効果

激光喷丸对提高大型焊接试件疲劳寿命的影响

• 发表时间: 2012
• 作者: 木下真一;鎌田敏郎;内田慎哉;崎野 良比呂
• 通讯作者: 崎野 良比呂

レーザピーニングの大型構造物への適用

激光喷丸在大型结构中的应用

• 发表时间: 2013
• 作者: 丸山泰蔵;斎藤隆泰;廣瀬壮一;崎野 良比呂
• 通讯作者: 崎野 良比呂

Application of LPwC to High-Strength Structural Steel and Its Weld Zone

LPwC在高强结构钢及其焊缝区的应用

• 发表时间: 2011
• 作者: 起塚亮輔;貝戸清之;伊藤哲男;西川秀;Hidetsugu Suto;Yoshihiro SAKINO
• 通讯作者: Yoshihiro SAKINO

レーザピーニングによる溶接継手の疲労強度向上-社会資本ストックのメンテナンスに向けて-

通过激光喷丸提高焊接接头的疲劳强度 - 用于维护社会资本存量 -

• 发表时间: 2013
• 作者: H.Shirato;K.Maeta;Y.Kato;Y.Takasugi;円田浩二;崎野 良比呂
• 通讯作者: 崎野 良比呂