Prediction of the Properties of Recycled Aggregate Concrete Based on the Estimation of Pore Volume

基于孔隙体​​积估算的再生骨料混凝土性能预测

• 批准号: 21560487
• 负责人: SAGAWA Yasutaka
• 金额: $ 2.75万
• 依托单位: Kyushu University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560487/
• 关键词: 再生骨材; 再生骨材コンクリート; 吸水率; 単位総水量; 細孔容積; 空隙; X線CT像; ビッカース硬度; 空隙量; 強度; リサイクル; 空隙構造; X線CT; 細孔構造

When the recycled aggregates with high water absorption was used, pore volume from 50nanometer to 2 micrometer formed in the new cement matrix increased. There was a good relationship between the ratio of cement content to total water in mixture and pore volume. In order to clarify the behavior of water moving from the inside of aggregates to the new cement matrix, micro-focus type X-ray CT scanner and Vicker' s hardness meter were used, and the area in which water affected was examined.

当使用具有高水吸收的回收聚集体时，在新的水泥基质中形成的孔体积从50nAnomer到2微米增加。水泥含量与混合物中的总水与孔体积的比率之间存在良好的关系。为了阐明从聚集体内部到新水泥矩阵的水的行为，使用了微焦点X射线CT扫描仪和Vicker的硬度计，并检查了受影响的水域。

项目成果

異種材料界面の可視化によるコンクリートの性能評価に関する研究

不同材料界面可视化评价混凝土性能研究

• 发表时间: 2010
• 作者: 佐川康貴;ほか;濱田秀則,佐川康貴
• 通讯作者: 濱田秀則,佐川康貴

骨材中の水分が再生骨材コンクリートの強度に及ぼす影響に関する研究

骨料水分对再生骨料混凝土强度影响的研究

• 发表时间: 2011
• 期刊: コンクリート工学年次論文集
• 作者: 佐川康貴;ほか
• 通讯作者: ほか