Surface effect on Li-ion diffusion in nano-sized electrodes

纳米电极中锂离子扩散的表面效应

• 批准号: 20810029
• 负责人: OKUBO Masashi
• 金额: $ 2.1万
• 依托单位: Chuo University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (Start-up)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20810029/
• 关键词: リチウムイオン2次電池; 電極; ナノサイズ効果; 正極材料; ナノ粒子; ナノイオニクス; リチウムイオン電池

High charge/discharge rate Li-ion batteries require short Li-ion diffusion length in electrodes, thus the nano-sized electrodes. The hydrothermal synthesis of the nano-sized electrodes such as LiCoO_2 or LiMn_2O_4 has been established in this study. Nano-sized LiCoO_2 has revealed to exhibit low charge/discharge capacity and voltage due to the surface Co(II) atom. In contrast, nano-sized LiMn_2O_4 showed higher charge/discharge capacity than the bulk one, since the surface energy compete with the lattice distortion during the redox process.

高电荷/放电速率锂离子电池需要短的电极中的锂离子扩散长度，因此需要纳米大小的电极。在本研究中已经建立了纳米大小的电极（例如LICOO_2或LIMN_2O_4）的热液合成。纳米大小的LICOO_2揭示了由于表面CO（II）原子而显示的低电荷/放电能力和电压。相比之下，纳米尺寸的LIMN_2O_4的充电/放电能力比散装量更高，因为表面能在氧化还原过程中与晶格失真竞争。

项目成果

LixMn2O4における2相共存領域へのナノサイズ効果の解析

纳米尺寸对 LixMn2O4 两相共存区域的影响分析

• 发表时间: 2009
• 作者: 大久保將史;工藤徹一;本間格;大久保將史
• 通讯作者: 大久保將史

ナノ正極活物質の水熱合成と高出力電極特性

纳米正极活性材料的水热合成及高功率电极性能

• 发表时间: 2008
• 作者: 大久保將史;工藤徹一;本間格
• 通讯作者: 本間格

水熱法を用いたリチウムイオン2次電池用ナノ正極材料の合成

水热法合成锂离子二次电池纳米正极材料

• 发表时间: 2008
• 作者: 大久保将史;他
• 通讯作者: 他

Determination of activatiaon energy for Li ion diffusion in electrodes.

电极中锂离子扩散活化能的测定。

• 发表时间: 2009
• 期刊: J. Phys. Chem. B 113
• 作者: M. Okubo;T. Kudo;H.S. Zhou;I. Honma
• 通讯作者: I. Honma

ナノサイズ電極におけるリチウムイオン拡散現象の解析

纳米电极中锂离子扩散现象分析

• 发表时间: 2009
• 作者: 大久保將史;工藤徹一;本間格
• 通讯作者: 本間格