Synthesis and evaluation of bi-modal composites by reactive arc-melting method.

反应电弧熔化法双峰复合材料的合成与评价。

• 批准号: 20560675
• 负责人: TSUDA Hiroshi
• 金额: $ 2.75万
• 依托单位: Osaka Prefecture University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20560675/
• 关键词: 二重複相組織; 新規Ti基合金; その場合成; 炭化チタン; 微細組織; 新規複合材料; TEM観察; 二重複相; TiC粒子; Ti析出; 高強度; TIC粒子

TiC particle dispersed Ti matrix composites were successfully synthesized by reactive arc-melting method from Ti, C and N (TiN powder or gaseous nitrogen) system. Plate-like α-Ti was precipitated in the resulting TiC particles. Therefore Vickers hardness was obviously decreased compared to that of a monolithic TiC. It seems to be considered that precipitated α-Ti enhances the ductility of the TiC particles and nitrogen solution strengthens the matrix Ti. Those results clearly show that new conceptual bi-modal Ti matrix composites can be synthesized by reactive arc-melting methods.

采用反应电弧熔炼法，以Ti、C和N（TiN粉末或气态氮）体系成功合成了TiC颗粒分散的Ti基复合材料，所得TiC颗粒中析出片状α-Ti，从而显着降低了维氏硬度。与整体 TiC 相比，似乎认为沉淀的 α-Ti 增强了 TiC 颗粒的延展性，而氮溶液则强化了基体 Ti。双峰Ti基复合材料可以通过反应电弧熔炼方法合成。

项目成果

Effect of Fe and N addition on microstructure of TiC particle in Ti matrix composites

Fe和N添加对Ti基复合材料中TiC颗粒微观结构的影响

• 发表时间: 2009
• 作者: G.Amirthan;K.Nakao;H.Tsuda;S.Mori
• 通讯作者: S.Mori

Catalytic properties of cold-rolled Ni_3(Si,Ti) intermetallic foils for methanol decomposition.

冷轧Ni_3(Si,Ti)金属间箔对甲醇分解的催化性能

• 发表时间: 2010
• 期刊: Materials Transactions 51
• 作者: Y.Kaneno;T.Kondo;Y.Fujimoto;H.Tsuda;Y.Xu;M.Demura;H.Iwai;T.Hirano;T.Takasugi
• 通讯作者: T.Takasugi

Valence state and spatial distribution of Fe ions in ferro-magnetic Ba(Fe_<1-x>Zrx)0_<3-δ> single-crystal films on SrTiO_3 substrates

SrTiO_3基片铁磁Ba(Fe_<1-x>Zrx)0_<3-δ>单晶薄膜中Fe离子的价态和空间分布

• 发表时间: 2008
• 期刊: Journal of Applied Physics 103
• 作者: T. Matsui;R. Sato;H. Tsuda
• 通讯作者: H. Tsuda

Ti/TiC複合材料巾のTiC粒子の微細組織変化に及ぼす熱処理の影響

热处理对Ti/TiC复合材料中TiC颗粒微观结构变化的影响

• 发表时间: 2009
• 作者: 中尾和幸;津田大;森茂生
• 通讯作者: 森茂生

α+βおよびβ-Ti 基複合材料におけるTi粒子の微細組織に及ぼすN 添加の影響

N添加对α+β和β-Ti基复合材料中Ti颗粒微观结构的影响

• 发表时间: 2010
• 作者: 関元航;津田大;森茂生
• 通讯作者: 森茂生