Preparation of highly dense and oriented nano-structured zeolite films from slow formation of microstructure using starting materials with low solubility

使用低溶解度起始材料缓慢形成微结构制备高致密定向纳米结构沸石膜

• 批准号: 20560626
• 负责人: MATSUDA Motohide
• 金额: $ 3万
• 依托单位: Kumamoto University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20560626/
• 关键词: ゼオライト; 膜作製プロセス; ナノ材料; 超薄膜; セラミックス

In this research project, highly oriented and nano-structured dense MFI-type of zeolite films were successfully fabricated using a glass powder as starting materials for hydrothermal synthesis. Our investigations revealed that the b-axis orientation appeared with transformation of amorphous to crystalline phase with an increase in hydrothermal treatment time. The transformation behavior was affected by pH of the reaction solutions. It was suggested from the results obtained that the transformation spread from the surface of the amorphous film.

在该研究项目中，使用玻璃粉作为水热合成的起始材料成功制造了高度定向和纳米结构的密集的沸石膜的密集型MFI型。我们的研究表明，随着水热治疗时间的增加，B轴取向出现，无定形转换为结晶相。转化行为受反应溶液的pH影响。从获得的结果表明，转化从无定形膜的表面扩散。

项目成果

ゼオライト配向膜の作製と細孔内修飾

沸石取向膜的制备及孔道改性

• 发表时间: 2008
• 作者: J.H.Eom;Y.W.Kim;M.Narisawa;乾由貴子
• 通讯作者: 乾由貴子

バルク状原料を用いたMFI型ゼオライト膜の作製

使用散装原料制备MFI型沸石膜

• 发表时间: 2010
• 作者: U. Mizutani;R. Asahi;H. Sato;T. Noritake;T. Takeuchi;稲富俊裕
• 通讯作者: 稲富俊裕

ガラス粉末からのゼオライト膜作製とその膜形成機構

玻璃粉制备沸石膜及其成膜机理

• 发表时间: 2011
• 作者: U.Mizutani;T.Noritake;T.Ohsuna;T.Takeuchi;稲富俊裕
• 通讯作者: 稲富俊裕

固体状原料を出発源としたMFI薄膜の作製と高次構造制御

从固体原材料开始的MFI薄膜的制造和高阶结构控制

• 发表时间: 2009
• 作者: M.Inukai;K.Soda;H.Sato;U.Mizutani;北智孝
• 通讯作者: 北智孝

ガラス粉末を出発材とした配向性MFI型ゼオライト薄膜の作製

以玻璃粉为原料制备定向MFI型沸石薄膜

• 发表时间: 2010
• 作者: 稲富俊裕