Estimation method on causes of crack in concrete used buildings based on drying shrinkage strain by oven drying

基于烘干收缩应变的混凝土旧房裂缝成因估算方法

• 批准号: 20560513
• 负责人: HASEGAWA Takuya
• 金额: $ 2.91万
• 依托单位: Hokkaido University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2010
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20560513/
• 关键词: コンクリート; 乾燥収縮ひずみ; ひび割れ; 強制乾燥; 仕上材; 環境条件; 乾燥収縮; 屋外暴露; レーザー変位計; 炭酸化収縮; 暴露試験

In this study, it was estimated the standard drying shrinkage strain of concrete in existing RC buildings based on results of oven dry shrinkage test for the core test pieces. And we studied the estimation method on causes of crack in concrete of buildings. From these results, we proposed the methods as follows ;(1)The testing methods of oven drying shrinkage stain from core test pieces(2)The estimation methods on drying shrinkage stain considering finishing materials and environmental conditions(3)The estimation methods on cases of crack in existing RC buildings based on (1) and (2)

在本研究中，根据核心试件的烘干收缩试验结果，估算了现有 RC 建筑中混凝土的标准干燥收缩应变。并研究了建筑物混凝土裂缝成因的估算方法。根据这些结果，我们提出了以下方法：（1）芯试件烘干收缩污点的测试方法（2）考虑饰面材料和环境条件的干燥收缩污点的估算方法（3）案例估算方法基于(1)和(2)的现有RC建筑物的裂缝

项目成果

札幌市における仕上材・表面改質材を施工したコンクリートの表層の温湿度変化

札幌市饰面材料和表面改性材料处理的混凝土表层的温度和湿度变化

• 发表时间: 2009
• 作者: 長谷川拓哉;千歩修
• 通讯作者: 千歩修

強制乾燥収縮試験に適用できる試験体寸法および長さ変化率測定方法の検討

适用于强制干燥收缩试验的试样尺寸和长度变化率测量方法的检验

• 发表时间: 2010
• 作者: 長谷川拓哉;千歩修
• 通讯作者: 千歩修

札幌市における仕上材・表面改質材を施工したコンクリート表層の温湿度変化

札幌市使用精加工和表面改性材料的混凝土表层的温度和湿度变化

• 发表时间: 2009
• 作者: 長谷川拓哉;千歩修
• 通讯作者: 千歩修

乾燥開始後50ヶ月のデータに基づく仕上塗材・表面改質材を施工したコンクリートの乾燥収縮性状

涂有饰面涂料和表面改性材料的混凝土的干燥收缩特性基于干燥开始后50个月的数据

• 发表时间: 2011
• 期刊: 日本コンクリート工学協会年次論文集 CD-ROM(採用決定)
• 作者: 長谷川拓哉;千歩修
• 通讯作者: 千歩修

乾燥指標体を用いたコンクリートの強制乾燥収縮試験の検討

利用干燥指示剂进行混凝土强制干燥收缩试验的研究

• 发表时间: 2010
• 期刊: 日本コンクリート工学協会年次論文集 CD-ROM
• 作者: 長谷川拓哉;千歩修
• 通讯作者: 千歩修