Ag/C包覆对Li[Li0.2Mn0.54Ni0.13Co0.13]O2电化学性能的影响

基本信息

DOI：
10.3866/pku.whxb201406251
发表时间：
2014-08
期刊：
物理化学学报
影响因子：
--
通讯作者：
高飞
中科院分区：
其他
文献类型：
--
作者： 薛庆瑞;李建玲;徐国峰;侯朋飞;晏刚;代宇;王新东;高飞研究方向： -- MeSH主题词： --
关键词： --
来源链接：pubmed详情页地址

文献摘要

A layered lithium-rich solid solution material Li[Li0.2Mn0.54Ni0.13Co0.13]O2 with an Ag/C coating layer was prepared by a method combining coprecipitation and elemental chemical deposition. The effects of the Ag/C coating layer on the electrochemical performance of Li[Li0.2Mn0.54Ni0.13Co0.13]O2 were studied by X-ray diffraction (XRD), field emission scanning electron microscopy (SEM), transmission electron microscopy (TEM), constant current charge-discharge, cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and X-ray energy dispersive spectroscopy (EDS). The results show that the thickness of the Ag/C coating layer is about 25 nm, and the Ag/C coating maintains the hexagonal layered structure of the solid solution material α -NaFeO2.
运用共沉淀和元素化学沉积相结合的方法，制备出了具有Ag／C包覆层的层状富锂固溶体材料Li[Li0.2Mn0.54Ni0.13Co0.13]O2．通过X射线衍射（XRD）、场发射扫描电子显微镜（SEM）、透射电子显微镜（TEM）、恒流充放电、循环伏安（CV），电化学阻抗谱（EIS）和X射线能量散射谱（EDS）方法，研究了Ag／C包覆层对Li[Li0.2Mn0.54Ni0.13Co0.13]O2电化学性能的影响．结果表明，Ag／C包覆层的厚度约为25nm，Ag／C包覆在保持了固溶体材料α-NaFeO2六方层状
参考文献（0）
被引文献（0）

数据更新时间：{{ references.updateTime }}

关联基金

碳载体诱导Schiff碱基氧化还原聚合物的结构生长控制及储能机理
批准号：
51372021
批准年份：
2013
资助金额：
80.0
项目类别：
面上项目
高飞
通讯地址:
--
所属机构:
--
电子邮件地址：
--
免责声明免责声明
1、猫眼课题宝专注于为科研工作者提供省时、高效的文献资源检索和预览服务；
2、网站中的文献信息均来自公开、合规、透明的互联网文献查询网站，可以通过页面中的“来源链接”跳转数据网站。
3、在猫眼课题宝点击“求助全文”按钮，发布文献应助需求时求助者需要支付50喵币作为应助成功后的答谢给应助者，发送到用助者账户中。若文献求助失败支付的50喵币将退还至求助者账户中。所支付的喵币仅作为答谢，而不是作为文献的“购买”费用，平台也不从中收取任何费用，
4、特别提醒用户通过求助获得的文献原文仅用户个人学习使用，不得用于商业用途，否则一切风险由用户本人承担；
5、本平台尊重知识产权，如果权利所有者认为平台内容侵犯了其合法权益，可以通过本平台提供的版权投诉渠道提出投诉。一经核实，我们将立即采取措施删除/下架/断链等措施。
我已知晓