Attempt of application of half-metal granular to spin transistor structure

半金属颗粒在自旋晶体管结构中的应用尝试

• 批准号: 22560308
• 负责人: JIMBO Mutsuko
• 金额: $ 2.75万
• 依托单位: Daido University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22560308/
• 关键词: 電気・電子材料(半導体); 誘電体; 磁性体; 超誘電体; 有機物; 絶縁体; 超伝導体; スピントランジスタ; グラニュラー膜; ハーフメタル; トンネル伝導; スピンエレクトロニクス

The granular films consisting of a ful-Heusler CFAS alloy and Al2O3 exhibited a large MR ratio of about 18% at room temperature. This value is the largest value ever reported for magnetic metal-insulator granular films. It was suggested that the large MR ratio was obtained owing to the existence of granules with L21 or B2 phases, which exhibit high spin polarization. This result showed the possibility of the application of the half-metal to the granular films.

由ful-Heusler CFAS合金和Al2O3组成的颗粒薄膜在室温下表现出约18%的大MR比。该值是迄今为止报道的磁性金属绝缘体颗粒薄膜的最大值。这表明，由于存在具有高自旋极化的 L21 或 B2 相颗粒，因此获得了大的 MR 比。这一结果表明了半金属在颗粒薄膜中应用的可能性。

项目成果

Co_2FeAl_Si_-MgF_2グラニュラー薄膜の構造とトンネル磁気抵抗効果

Co_2FeAl_<0.5>Si_<0.5>-MgF_2颗粒薄膜的结构及隧道磁阻效应

• 发表时间: 2011
• 作者: 浦川依久; 尾崎正太郎; 藤原裕司; 小原直人; 前田浩二; 加藤剛志; 神保睦子; 小林正
• 通讯作者: 小林正

Co2FeAl0.5Si0.5-MgF2グラニュラー薄膜の構造とトンネル磁気抵抗効果

Co2FeAl0.5Si0.5-MgF2颗粒薄膜的结构与隧道磁阻效应

• 发表时间: 2011
• 作者: 浦川依久;尾崎正太郎;藤原裕司;小原直人;前田浩二;加藤剛志;神保睦子;小林正
• 通讯作者: 小林正

Magnetoresistance of Co_2FeAi_Si_-MgF_2 granular films

Co_2FeAl_<0.5>Si_<0.5>-MgF_2颗粒薄膜的磁阻

• 发表时间: 2010
• 作者: Y.Fujiwara; S.Ozaki; Y.Urakawa; K.Sato; M.Kondo; M.Jimbo; T.Kato; T.Kobayashi
• 通讯作者: T.Kobayashi

Magnetoresistance and electronic structure of granular films with MgO or MgF2 matrices

MgO 或 MgF2 基体颗粒薄膜的磁阻和电子结构

• DOI: 10.1088/1742-6596/266/1/012087
• 发表时间: 2011
• 作者: Y.Fujiwara; H.Matsuda; K.Sato; M.Jimbo; T.Kobayashi
• 通讯作者: T.Kobayashi

Tunnel Magnetoresistance of CoFeAlSi-AlO Granular Films

CoFeAlSi-Al2O颗粒薄膜的隧道磁阻

• 发表时间: 2011
• 作者: M.Kondo; T.Chino; Y.Fujiwara; M.Jimbo
• 通讯作者: M.Jimbo