Examination based on Thermal Engineering for Improvement of Manufacturing Process of High Tensile Strength Steel

基于热工学的高强度钢制造工艺改进检验

• 批准号: 21560224
• 负责人: OHTAKE Hiroyasu
• 金额: $ 3.24万
• 依托单位: Kogakuin University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21560224/
• 关键词: 対流; 沸騰; 鉄鋼製造プロセス; クエンチ; 熱工学; 赤外線放射温度計; 膜沸騰崩壊温度; 熱力学過熱限界壊温度; 冷却モデル; 非接触計測

In order to improve manufacturing process of High Tensile Strength Steel for vehicle body, the purposes of the present research was prediction of boiling heat transfer and clarification of cooling process under manufacturing steel. The present experimental results showed that sputtering temperature was close to the thermodynamic limit of liquid superheat, 300℃. The behavior of rewetting on high superheated surface was also simulated by using the transient heat conduction with the conventional correlations of boiling heat transfer.

为了改进车身用高强度钢的制造工艺，本研究的目的是预测制造钢时的沸腾传热和冷却过程，目前的实验结果表明溅射温度接近热力学极限。液体过热度，300℃，还利用瞬态热传导与沸腾传热的常规关系式模拟了高过热度表面的再润湿行为。

项目成果

高温加熱面の膜沸騰崩壊温度に関する研究

高温受热面膜沸腾崩溃温度研究

• 发表时间: 2010
• 作者: 永嶌望(大竹浩靖)

二次元温度場計測を通した高温加熱面膜沸騰崩壊温度条件の定量化と膜沸騰崩壊条件のモデル解析に関する研究【招待講演】

通过二维温度场测量和膜沸腾崩塌条件模型分析对高温受热面膜沸腾崩塌温度条件进行量化研究[特邀报告]

• 发表时间: 2011
• 作者: 大竹浩靖

高温加熱面の濡れ開始機構に関する研究

高温受热面润湿引发机理研究

• 发表时间: 2012
• 作者: 大堀哲矢(大竹浩靖)

二次元温度場計測を通した高温加熱面膜沸騰崩壊温度条件に関する研究

二维温度场测量研究高温受热面膜沸腾溃灭温度条件

• 发表时间: 2011
• 作者: 小泉安郎(大竹浩靖)

高温加熱面の膜沸騰崩壊温度に関する研究

高温受热面膜沸腾崩溃温度研究

• 发表时间: 2010
• 作者: 永嶌望(大竹浩靖)