Magnetization reversal control of FePt perpendicular media by energy assist

FePt垂直介质的能量辅助磁化反转控制

• 批准号: 23686100
• 负责人: TAKAHASHI Yukiko
• 金额: $ 13.98万
• 依托单位: National Institute for Materials Science
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (A)
• 财政年份: 2011
• 资助国家: 日本
• 起止时间: 2011-04-01 至 2014-03-31
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-23686100/
• 关键词: エネルギーアシスト磁化反転; FePt; エネルギーアシスト

We made FePt based granular film with various nonmagnetic matrix in order to realize well separated microstructure with the columnar structure. By using Cr2O3 as a nonmagnetic matrix, we successfully obtained well-isolated microstructure with the average particle size of 6 nm and the aspect ratio more than 1.5 in FePt-Cr2O3 granular film. It showed the perpendicular Hc of 20 kOe with strong perpendicular anisotropy. In addition, by applying RF magnetic field Hc reduction from 6 kOe to 4.5 kOe was observed in FePt-C granular film with the perpendicular anisotropy of 1*107 erg/cc.

我们用各种非磁性基体制作了 FePt 基颗粒薄膜，以实现与柱状结构良好分离的微观结构。以Cr2O3为非磁性基体，在FePt-Cr2O3颗粒薄膜中成功获得了平均粒径为6 nm、长宽比大于1.5的隔离良好的微观结构。其垂直Hc为20 kOe，具有很强的垂直各向异性。此外，通过施加射频磁场，在垂直各向异性为1*107 erg/cc的FePt-C颗粒膜中观察到Hc从6 kOe降低到4.5 kOe。

项目成果

L1_0 ordered FePt based double-layerd perpendicular recording media

L1_0有序FePt基双层垂直记录介质

• 发表时间: 2012
• 作者: B. Varaprasad;Y.K. Takahashi and K. Hono
• 通讯作者: Y.K. Takahashi and K. Hono

FePt-Cr_2O_<3 >の微細構造と磁気特性

FePt-Cr_2O_<3>的显微组织与磁性能

• 发表时间: 2013
• 作者: 城山泰祐;B. Varaprasad,高橋有紀子、宝野和博
• 通讯作者: B. Varaprasad,高橋有紀子、宝野和博

Microstructure and magnetic properties of B-added FePt-C thin films for perpendicular magnetic recording media

垂直磁记录介质用B添加FePt-C薄膜的微观结构和磁性能

• 发表时间: 2013
• 作者: W.B. Cui;B.S.D.Varaprasad;Y.K. Takahashi;T. Shiroyama;K. Hono
• 通讯作者: K. Hono

FePt磁気記録媒体

FePt磁记录介质

• 发表时间: 2013

Microstructure control of L1_0 ordered FePt granular film for Heat-Assisted Magnetic Recording (HAMR) media B. Varaprasad, Y.K

用于热辅助磁记录 (HAMR) 介质的 L1_0 有序 FePt 颗粒薄膜的微观结构控制 B. Varaprasad, Y.K

• 发表时间: 2013
• 期刊: JOM
• 影响因子: 2.6
• 作者: K. Bushimata;S.–I. Ogino;K. Hirano;T. Yabune;K. Sato;T. Itoh;K. Motomiya;K. Yokoyama;D. Mabuchi;H. Nishizaka;G. Yamamoto;T. Hashida;K. Tohji;Y. Sato;Takahashi and K. Hono
• 通讯作者: Takahashi and K. Hono