Quantitative characterization of Nanogranular film using contrast variation between small-angle X-ray and neutron scattering

利用小角 X 射线和中子散射之间的对比度变化对纳米颗粒薄膜进行定量表征

• 批准号: 22604003
• 负责人: OBA Yojiro
• 金额: $ 2.75万
• 依托单位: Kyoto University (2012)National Institute for Materials Science (2010-2011)
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22604003/
• 关键词: 中性子小角散乱; X線小角散乱; ナノグラニュラー; 合金コントラスト変調法; 中性子小角散乱法; X線小角散乱法; 量子ビーム; ナノ材料; 小角散乱; 複合材料・物性; 中性子小角散乱; X線小角散乱; ナノグラニュラー; 合金コントラスト変調法; 中性子小角散乱法; X線小角散乱法; 量子ビーム; ナノ材料; 小角散乱; 複合材料・物性

Since nanostructure of nanogranular films are closely related with their physical properties, the quantitative characterization of the nanostructure is an important issue. In this study, the analysis method using small-angle neutron and X-ray scattering has been utilized. As a result, the size distribution and the dispersion states of the nanoparticles in the nanogranular films were quantitatively evaluated. In addition, the partitioning state of chemical composition between the nanoparticles and the matrix was quantitatively analyzed.

由于纳米膜的纳米结构与其物理特性密切相关，因此纳米结构的定量表征是一个重要问题。在这项研究中，已经使用了使用小角度中子和X射线散射的分析方法。结果，对纳米膜中纳米颗粒的尺寸分布和分散态进行了定量评估。另外，对纳米颗粒和基质之间的化学组成状态进行了定量分析。