Growth of single-crystal films of suboxides on the surfaces of refractory metals with a cubic system

立方系难熔金属表面低氧化物单晶薄膜的生长

• 批准号: 22550127
• 负责人: EDAMOTO Kazuyuki
• 金额: $ 3万
• 依托单位: Rikkyo University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Scientific Research (C)
• 财政年份: 2010
• 资助国家: 日本
• 起止时间: 2010 至 2012
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-22550127/
• 关键词: 表面・界面物性; 超薄膜; 化学物理; MBE・エピタキシャル; MBE、エピタキシャル

Growth of films of a TiO single-crystal, which is hard to synthesize in an atmospheric condition, has been investigated with the use of Mo(100) substrate. It was found that the epitaxial TiO film can be formed by Ti deposition on Mo(100) and subsequent oxidation of the Ti film by 12 L of O2 exposure,and the annealing of the film at higher than 1100℃. The two-dimensional band structure of a (2 ×2)TiO/Mo(100) system was investigated by angle-resolved PES, and it was found that the (2 × 2) system includes the TiO film with a (1 × 1) periodicity with respect to the Mo(100) substrate as well as the (2 ×2)-O/Mo(100) system.

使用MO（100）底物研究了TIO单晶膜的生长，在大气条件下很难合成。发现外延TIO膜可以通过TI沉积在MO（100）上形成（100），然后通过12 L的O2暴露对Ti膜进行氧化，并以高于1100℃的高度将薄膜退火。通过角度分辨PES研究了A（2×2）TIO/MO（100）系统的二维条带结构，发现（2×2）系统包括具有（1×1）周期性的TIO膜相对于MO（100）底物以及（2×2）-O/MO（2×2）-O/MO（100）系统。

项目成果

Mo(100)上に作成した Ti 酸化物超薄膜の電子状態

Mo(100)上超薄Ti氧化膜的电子态

• 发表时间: 2013
• 作者: 枝元一之;宗像紫織;今西沙織;掛札洋平; 長谷川智;小澤健一
• 通讯作者: 小澤健一

Mo(100)面上におけるTiO超薄膜の作成

Mo(100)表面超薄TiO薄膜的制备

• 发表时间: 2011
• 作者: 長谷川智;掛札洋平;枝元一之;小澤健一
• 通讯作者: 小澤健一

Mo(100)上に作成したTi超薄膜の酸化により生成する周期的酸化物

Mo(100)上超薄Ti膜氧化产生的周期性氧化物

• 发表时间: 2010
• 作者: 長谷川智;掛札洋平;枝元一之;小澤健一
• 通讯作者: 小澤健一

人工酸化物薄膜の作成とその電子状態解析

人造氧化物薄膜的制备及其电子结构分析

• 发表时间: 2012
• 作者: 枝元一之

Ag(100)表面に作成したTi酸化物薄膜のSTM観察

Ag(100)表面生成的Ti氧化物薄膜的STM观察

• 发表时间: 2012
• 作者: 掛札洋平;宗像紫織;増田成悟;枝元一之;小板谷貴典;吉本真也;吉信淳
• 通讯作者: 吉信淳