Study on mechanical property prediction model of cold sprayed coating

冷喷涂层力学性能预测模型研究

• 批准号: 21760573
• 负责人: ICHIKAWA Yuji
• 金额: $ 2.66万
• 依托单位: Tohoku University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2009
• 资助国家: 日本
• 起止时间: 2009 至 2011
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-21760573/
• 关键词: 溶射; コーティング; 粒子積層プロセス; コールドスプレー; 密着強度; オージェ電子分光分析

This work investigated dominant factor on mechanical properties of cold sprayed coating. Local area bonding, which is occurred in true contact area in particle interface is key mechanism of cold spray coating. True contact area bears material strength of cold sprayed coating. However, true contact bonding is weaker than ideal metallic bonding. Moreover, the density of cold spray coating is lower than that of bulk material. The density reduction is mainly occurred in true contact area. From these experimental evidences, the microstructure of true contact area is also important factor of mechanical property. Therefore, materials strength of cold spray is controlled by true contact area and interface structure of its.

本工作研究了影响冷喷涂涂层力学性能的主导因素。局部区域结合发生在颗粒界面的真实接触区域，是冷喷涂的关键机理。真实接触面积承受冷喷涂层的材料强度。然而，真正的接触接合比理想的金属接合弱。而且，冷喷涂涂层的密度比块状材料低。密度降低主要发生在真实接触区域。从这些实验证据来看，真实接触区域的微观结构也是机械性能的重要因素。因此，冷喷涂材料的强度是由其真实接触面积和界面结构控制的。

项目成果

コールドスプレー法で形成した銅薄膜の強度物性支配因子の解明

冷喷涂铜薄膜强度和物理性能影响因素的阐明

• 发表时间: 2012
• 作者: 渡邊雄亮;市川裕士;野中勇;三浦英生
• 通讯作者: 三浦英生

微視組織に着目したコールドスプレー銅積層体の強度特性評価

关注微观结构的冷喷涂铜层压板强度特性评价

• 发表时间: 2011
• 作者: 市川裕士;種村駿;野中勇
• 通讯作者: 野中勇

熱処理がコールドスプレー銅積層体の機械的特性に与える影響

热处理对冷喷铜层压板力学性能的影响

• 发表时间: 2011
• 作者: 渡邊雄亮;市川裕士;野中勇;三浦英生
• 通讯作者: 三浦英生

コールドスプレー法で作製した銅皮膜の密着強度

冷喷涂法铜膜的附着力

• 发表时间: 2011
• 作者: 渡邊雄亮;市川裕士;野中勇;三浦英生
• 通讯作者: 三浦英生

コールドスプレー銅皮膜の強度特性とその発現機構

冷喷铜镀层的强度特性及其发展机制

• 发表时间: 2011
• 作者: 種村駿;市川裕士;野中勇
• 通讯作者: 野中勇