• 批准号: 20740197
• 负责人: KOTEGAWA Hisashi
• 金额: $ 2.75万
• 依托单位: Kobe University
• 依托单位国家: 日本
• 项目类别: Grant-in-Aid for Young Scientists (B)
• 财政年份: 2008
• 资助国家: 日本
• 起止时间: 2008 至 2009
• 项目状态: 已结题
• 来源: https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-20740197/
• 关键词: 鉄系超伝導体; 圧力技術; 圧力効果; NMR; 鉄系超伝導; 高圧

We investigated the pressure effects on Fe-based superconductors through the resistivity and NMR measurement using the pressure cell which can apply the pressure above 4GPa. In FeSe, the superconducting transition temperature of 8K at ambient pressure increased to 37K, and the pressure dependence showed a plateau around 1GPa. In SrFe_2As_2, we found the critical pressure above which superconductivity appears is sensitive to the uniaxial stress along the c-axis. In addition, we found the transition temperature of 37K in Sr_2VFeAsO_3 increases to 46K under pressure.

我们使用压力电池通过电阻率和NMR测量来研究对基于Fe的超导体的压力影响，该压力电池可以将压力施加到4GPA以上的压力。在FESE中，在环境压力下8K的超导过渡温度增加到37K，压力依赖性显示出1GPA左右的高原。在SRFE_2AS_2中，我们发现超导性似乎对沿C轴的单轴应力敏感的临界压力。此外，我们发现在压力下，SR_2VFEASO_3中37K的过渡温度增加到46K。

项目成果

単結晶SrFe_2As_2における圧力誘起超伝の研究

单晶SrFe_2As_2压力诱导超透射研究

• 发表时间: 2009
• 作者: Mizoo;et al.;小手川恒
• 通讯作者: 小手川恒

鉄系物質で圧力誘起高温超伝導が実現

在铁基材料中实现压力诱导高温超导

• 发表时间: 2009
• 期刊: パリティ 8
• 作者: Hidekazu Mukuda;et al.;小手川恒
• 通讯作者: 小手川恒

11系および21113系鉄系超伝導体の圧力効果とNMR, 新規材料による高温超伝導基盤技術

11系列和21113系列铁基超导体的压力效应和核磁共振，新材料高温超导基础技术

• 发表时间: 2009
• 作者: H. Okabe;S. Yano;T. Muranaka;J. Akimitsu;小手川恒
• 通讯作者: 小手川恒

NMR and resistivity studies under pressure in FeSe

FeSe 压力下的 NMR 和电阻率研究

• 发表时间: 2009
• 作者: Akihiro Kondo;Junfeng Wang;Koichi Kindo;Tomoaki Takesaka;Yukihiro Kawamura;Takashi Nishioka;Daiki Tanaka;Hiroshi Tanida;Masafumi Sera;Y.Fujihara;H. Kotegawa
• 通讯作者: H. Kotegawa

NMR and resistivity studies under pressure in Fe-based

铁基压力下的核磁共振和电阻率研究

• 发表时间: 2009
• 作者: K. Noda;A. Koga;N. Kawakami;and Th. Pruschke;H. Kotegawa
• 通讯作者: H. Kotegawa